Ti‒50.13Ni and Ti‒49.62Ni (at.%) shape memory alloy ribbons were fabricated by melt-spinning method at different circumferential wheel velocities. The effects of wheel velocity, chemical composition and heat treatments on microstructure and Transformation temperature were investigated. Differences in wheel velocity led to differences in cooling rate and sample dimension, as well as in phase transformation temperatures. Two heat treatment conditions were studied, 350°C for 1h and 350°C for 5h. In the samples produced at high wheel velocity and heat-treated at 350°C for 5h, nanosized Ti-rich precipitates were observed in both chemical compositions. Cross-sectional microstructure was studied by optical microscopy; SEM was used to study the nanometric grains and nano precipitation. The transformation temperatures were analyzed by DSC.

In this research, an ion milling equipment was used to elaborate nanoparticles from Cu-Zn-Al alloys with shape memory effect. Two different compositions were used, target A: 75.22Cu-17.12Zn-7.66Al at % with an Ms of -9 °C and target B: 76.18Cu-15.84Zn-7.98Al with an Ms of 20 °C. Nanoparticles were characterized by High Resolution Transmission Electron Microscopy, Electron Diffraction and Energy Dispersive X-ray Spectroscopy. The obtained nanoparticles showed a small dispersion, with a size range of 3.2-3.5 nm. Their crystal structure is in good agreement with the bulk martensitic structure of the targets. In this sense, results on morphology, composition and crystal structure have indicated that it is possible to produce nanoparticles of CuZnAl shape memory alloys with martensitic structure in a single process using Ion Milling.